🕑 Added 2023-02-02 21:00:21 +0000 UTCI think I figured out how to turn the brittle cast iron I've been producing into malleable iron that can be forged flat. When ever I smelt local ores it always produces cast iron prills rather than softer blooms of low carbon iron as one would expect from the bloomery process. I believe this because the prills are very hard, but when struck hard enough they shatter rather than flatten.
Cast iron is iron that has a high carbon content (when arranged by carbon content: Cast iron>Steel>iron). Cast iron has a lower melting point and is harder compared to regular iron. But it is more brittle so it's nearly impossible to forge. So I figured out how to decarburize it after some experiments.
First I tried making an ingot to work on but it didn't cast properly. Then I tried rusting the iron to oxidize the metal before melting so it would decarburize the cast iron during the melt (similar to the "wet puddling" process in metallurgy). But this gave an incomplete melt also.
The method that finally worked was simply melting the cast iron in front of the air blast till the carbon burnt out in the oxygen rich zone of the forge. This caused the cast iron prills to melt together in a single blob that I then was able to hammer flat while yellow hot.
This method is similar to the "stir fried steel/ 炒钢" process in ancient China or the "Osmond process" in Europe. It's done where ever cast iron needs to be converted to a lower carbon to be forged. I've seen videos about carburizing iron on youtube but none about decarburizing cast iron Much appreciated.
Comments
Primitive Technology
Thanks Destin, just sent you my email address. John.
Smarter Every Day
Hey man, Destin here. I’d love to get in touch with you about something interesting you may want to do.
Primitive Technology
Thanks for that. You're right, I don't think it's as dangerous as they say. Much appreciated.