Steel: A Symphony of Industry 1936 American Iron and Steel Institute
🕑 Added 2019-04-29 17:24:46 +0000 UTCmore at http://quickfound.net/
Originally a public domain film, slightly cropped to remove uneven edges, with the aspect ratio corrected, and one-pass brightness-contrast-color correction & mild video noise reduction applied.
The soundtrack was also processed with volume normalization, noise reduction, clipping reduction, and/or equalization (the resulting sound, though not perfect, is far less noisy than the original).
https://en.wikipedia.org/wiki/History_of_the_steel_industry_ (1850–1970)
Wikipedia license: http://creativecommons.org/licenses/by-sa/3.0/
The history of the modern steel industry began in the late 1850s; steel has became a staple of the world's industrial economy. This article is intended only to address the business, economic and social dimensions of the industry, since the bulk production of steel began as a result of Henry Bessemer's development of the Bessemer converter, in 1857. Previously, steel was very expensive to produce, and only used in small, expensive items, such as knives, swords and armor...
Technology
Steel is an alloy composed of between 0.2 and 2.0 percent carbon, with the balance being iron. From prehistory through the creation of the blast furnace, iron was produced from iron ore as wrought iron, 99.82 - 100 percent Fe, and the process of making steel involved adding carbon to iron, usually in a serendipitous manner, in the forge, or via the cementation process. The introduction of the blast furnace reversed the problem. A blast furnace produces pig iron — an alloy of approximately 90 percent iron and 10 percent carbon. When the process of steel-making is started with pig iron, instead of wrought iron, the challenge is to remove a sufficient amount of carbon to reduce it to the 0.2 to 2 percentage for steel.
Before about 1860, steel was an expensive product, made in small quantities and used mostly for swords, tools and cutlery; all large metal structures were made of wrought or cast iron. Steelmaking was centered in Sheffield and Middlesbrough, Britain, which supplied the European and American markets. The introduction of cheap steel was due to the Bessemer and the open hearth processes, two technological advances made in England. In the Bessemer process, molten pig iron is converted to steel by blowing air through it after it was removed from the furnace. The air blast burned the carbon and silicon out of the pig iron, releasing heat and causing the temperature of the molten metal to rise. Henry Bessemer demonstrated the process in 1856 and had a successful operation going by 1864. By 1870 Bessemer steel was widely used for ship plate. By the 1850s, the speed, weight, and quantity of railway traffic was limited by the strength of the wrought iron rails in use. The solution was to turn to steel rails, which the Bessemer process made competitive in price. Experience quickly proved steel had much greater strength and durability and could handle the increasingly heavy and faster engines and cars.
After 1890 the Bessemer process was gradually supplanted by open-hearth steelmaking and by the middle of the 20th century was no longer in use. The open-hearth process originated in the 1860s in Germany and France. The usual open-hearth process used pig iron, ore, and scrap, and became known as the Siemens-Martin process. Its process allowed closer control over the composition of the steel; also, a substantial quantity of scrap could be included in the charge. The crucible process remained important for making high-quality alloy steel into the 20th century. By 1900 the electric arc furnace was adapted to steelmaking and by the 1920s, the falling cost of electricity allowed it to largely supplant the crucible process for specialty steels...